» Passive properties of duplex stainless steels after long-time ageing in air
|
|
HALINA KRAWIEC  VINCENT VIGNAL OLIVIER HEINTZ JEROME PEULTIER DOMINIQUE MAINY
The infl uence of long-term ageing in air on the chemical composition of passive fi lms and the electrochemical
behaviour of samples was investigated. After mechanical polishing, there is no signifi cant infl uence of the grain
orientation. The passive fi lm thickness is around 1.8 and 2.3 nm the ferrite and the austenite, respectively. The ratio
Cr/Fe in the passive fi lm is 0.48 and 0.37 in the ferrite and the austenite, respectively. The behaviour of both phases
behave can be described by the CPE. After long-term ageing, the passive fi lm thickness and the ratio Cr/Fe was not
signifi cantly affected. By contrast, LEIS diagrams were signifi cantly different than after mechanical polishing. Two
capacitive loops were detected in the ferrite phase associated with the passive fi lm and interface. The grain orientation
had signifi cant infl uence on the electrochemical behaviour of the ferrite phase after long-term ageing. On the
other hand, the austenite behaves like a blocking electrode represented by the Randles circuit.
Keywords: duplex stainless steel, EBSD, LEIS, microstructure, passivity
Charakterystyka właściwości pasywnych stali duplex starzonych w powietrzu
W pracy przedstawiono wpływ starzenia w powietrzu stali duplex UNS S32304 na jej elektrochemiczne zachowanie się i skład
chemiczny warstwy pasywnej. Wykazano, że orientacja krystalografi czna ziaren nie miała istotnego wpływu na elektrochemiczne
zachowanie się stali niestarzonej. Grubość warstwy pasywnej utworzonej na ferrycie była 1,8 nm, natomiast na austenicie 2,3 nm.
Z kolei stosunek Cr/Fe dla ferrytu wynosił 0,48, a dla austenitu 0,37. Starzenie próbek stali duplex w powietrzu przez 1 rok nie
wpłynęło istotnie na grubość warstwy pasywnej ani na stosunek Cr/Fe. Lokalne badania impedancyjne wykonane dla ferrytu
wykazywały obecność dwu pojemnościowych półokręgów, których nie obserwowano dla próbek niestarzonych. Ponadto wykazano,
że orientacja krystalografi czna ziaren ma wpływ[...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2010/11
|
|
|
» Korozja magnezu i stopu AZ91 w wodnych roztworach jonów chlorkowych i siarczanowych
|
|
HALINA KRAWIEC IWONA KOT JANUSZ LELITO JACEK BANAŚ
Magnez i stop magnezu AZ91 ulegają aktywnemu roztwarzaniu w wodnych
roztworach zawierających jony chlorkowe. Stop magnezu AZ91 dzięki obecności
fazy β-Mg17Al12 ma lepszą odporność na korozję niż czysty magnez.
Faza β-Mg17Al12 ulega pasywacji, co utrudnia korozję materiału. Badania
chronoamperometryczne wykazały, że na korozję najbardziej podatna jest
osnowa α-Mg.
Słowa kluczowe: magnez, AZ91, mikrostruktura, korozja lokalna
Corrosion behaviour of magnesium and AZ91 alloy in aqueous solution containing
chloride and sulfates ions
Magnesium and magnesium alloy AZ91 undergo the active dissolution in the aqueous
solution containing the chloride and sulfate ions. The higher corrosion resistance of
AZ91 alloy than pure magnesium is related with the presence of β-Mg17Al12 phase.
This phase easily undergoes the passivation process and hinder the corrosion of alloy.
Chronoaperometry measurements have revealed that the matrix α-Mg is the most
susceptible to corrosion 0.1M Na2SO4.
Keywords: magnesium, AZ91, microstructure, local corrosion
ochrona przed korozja 7/2011
1. Wstęp
Stopy magnezu ze względu na stosunkowo
dobre właściwości mechaniczne i małą gęstość,
znajdują zastosowanie głównie w przemyśle
samochodowym, lotniczym, elektronice
itp. Pomimo dobrych właściwości mechanicznych,
stopy magnezu wykazują wysoką podatność
na korozję, co jest przyczyną [...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2011/7
|
|
|
» Wpływ geometrii kapilary na widma otrzymane techniką lokalnej elektrochemicznej spektroskopii impedancyjnej
|
|
|
VINCENT VIGNAL HALINA KRAWIEC PAULINA ERAZMUS OLIVIER POLITANO
W pracy przedstawiono wpływ geometrii kapilary (średnicy, długości) na
kształt lokalnych widm impedancyjnych zarejestrowanych dla czystej platyny
w 0,1 M roztworze siarczanu VI sodu. Lokalne widma impedancyjne
wykonane za pomocą Techniki Elektrochemicznego Mikro-ogniwa zostały
porównane z widmami zarejestrowanymi w klasycznym trójelektrodowym
układzie.
Słowa kluczowe: lokalna elektrochemiczna spektroskopia impedancyjna,
techniki mikro-kapilarne, elektrochemia na granicy faz
Infl uence of the capillary geometry on the local electrochemical impedance spectroscopy
measurements
In the present paper, the infl uence of the capillary geometry (diameter and length) on
EIS measurements was investigated on pure platinum immersed in 0.1M Na2SO4 solution.
In addition, impedance data obtained using capillaries and the electrochemical
microcell technique were compared to those obtained with a classical three-electrode
cell.
Keywords: local electrochemical impedance spectroscopy, capillary techniques, interfacial
electrochemistry
ochrona przed korozja 7/2011
1. Introduction
Conventional electrochemical impedance
spectroscopy (EIS) has been used for more
than 40 years for studying electrochemical
mechanisms occurring at the electrode/electrolyte
interface. However, this technique is
limited to surface-averaged measurements
which account for the behaviour of the whole
electrode surface. In corrosion problems, such
as in localized corrosion, the response associated
with local phenomena (pitting, crevice
corrosion, breakdown of the passive fi lm, etc.)
cannot be extracted from the global impedance
diagrams. To overcome these diffi culties,
several scanning techniques using microelectrodes
have been developed. Among them, the
local electrochemical impedance spectroscopy
(LEIS) performed on restricted active areas
was pioneered by Isaacs et al. [1-3]. The local
[...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2011/7
|
|
|
|
|
|
» Infl uence of microstructure and Laser Shock Processing (LSP) on the corrosion behaviour of AA2050-T8
|
|
|
VINCENT VIGNAL HASSAN AMAR HALINA KRAWIEC PATRICE PEYRE LUIS FREDERICO DICK
The corrosion behaviour of AA2050-T8 was studied after polishing and after LSP treatment using microcapillaries
and the SVET. After polishing, both pitting at constituent particles and intergranular corrosion were observed. By
contrast, no intergranular corrosion / pits developed in the matrix after LSP. In addition, there is an anodic shift of
the pitting potential of sites containing particles. Benefi cial infl uence of LSP on corrosion behaviour of AA2050-T8
was also demonstrated using the SVET. The local current was systemically lower after LSP treatment.
Keywords: aluminium alloys, SVET, microstructure, corrosion, capillary techniques
Wpływ mikrostruktury i obróbki laserowej (LSP) na korozyjne zachowanie stopu AA2050-T8
Korozyjne zachowanie się stopu aluminium AA2050-T8 było badane po mechanicznym polerowaniu i po obróbce laserowej, za
pomocą Techniki Skaningowej Elektrody Wibrującej (SVET) i mikro-kapilar. Na próbkach polerowanych zaobserwowano korozję
wżerową i międzykrystaliczną w 0,1M NaCl. Z kolei osnowa próbek poddanych obróbce laserowej była odporna na korozję
międzykrystaliczną i wżerową. Dla miejsc zawierających wydzielenia obserwowano przesunięcie potencjału przebicia w kierunku
anodowym. Korzystny wpływ obróbki laserowej na odporność korozyjną stopu aluminium AA2050-T8 wykazały badania za pomocą
SVET. Dla próbek po laserowej obróbce zawsze rejestrowano niższy prąd niż dla próbek polerowanych.
Słowa kluczowe: stopy aluminium, SVET, mikrostruktura, korozja, techniki mikrokapilarne
1. Introduction
Aluminium alloys are a very important category
of materials because of their high mechanical
properties and wide range of industrial
applications. Aluminium alloys are prone to
microstructural corrosion (pitting corrosion,
intergranular corrosion, etc.). Microstructural
corrosion is caused by the presence of intermetallic
particles which may be either anodic
or cathodic with respect to the matrix. Microelectrochemical
techniqu[...]