» Passive properties of duplex stainless steels after long-time ageing in air
|
|
HALINA KRAWIEC  VINCENT VIGNAL OLIVIER HEINTZ JEROME PEULTIER DOMINIQUE MAINY
The infl uence of long-term ageing in air on the chemical composition of passive fi lms and the electrochemical
behaviour of samples was investigated. After mechanical polishing, there is no signifi cant infl uence of the grain
orientation. The passive fi lm thickness is around 1.8 and 2.3 nm the ferrite and the austenite, respectively. The ratio
Cr/Fe in the passive fi lm is 0.48 and 0.37 in the ferrite and the austenite, respectively. The behaviour of both phases
behave can be described by the CPE. After long-term ageing, the passive fi lm thickness and the ratio Cr/Fe was not
signifi cantly affected. By contrast, LEIS diagrams were signifi cantly different than after mechanical polishing. Two
capacitive loops were detected in the ferrite phase associated with the passive fi lm and interface. The grain orientation
had signifi cant infl uence on the electrochemical behaviour of the ferrite phase after long-term ageing. On the
other hand, the austenite behaves like a blocking electrode represented by the Randles circuit.
Keywords: duplex stainless steel, EBSD, LEIS, microstructure, passivity
Charakterystyka właściwości pasywnych stali duplex starzonych w powietrzu
W pracy przedstawiono wpływ starzenia w powietrzu stali duplex UNS S32304 na jej elektrochemiczne zachowanie się i skład
chemiczny warstwy pasywnej. Wykazano, że orientacja krystalografi czna ziaren nie miała istotnego wpływu na elektrochemiczne
zachowanie się stali niestarzonej. Grubość warstwy pasywnej utworzonej na ferrycie była 1,8 nm, natomiast na austenicie 2,3 nm.
Z kolei stosunek Cr/Fe dla ferrytu wynosił 0,48, a dla austenitu 0,37. Starzenie próbek stali duplex w powietrzu przez 1 rok nie
wpłynęło istotnie na grubość warstwy pasywnej ani na stosunek Cr/Fe. Lokalne badania impedancyjne wykonane dla ferrytu
wykazywały obecność dwu pojemnościowych półokręgów, których nie obserwowano dla próbek niestarzonych. Ponadto wykazano,
że orientacja krystalografi czna ziaren ma wpływ[...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2010/11
|
|
|
» Passivity of duplex stainless steels after long-term ageing in 0.5 M NaCl at 50°C
|
|
HUAYU ZHANG VINCENT VIGNAL OLIVIER HEINTZ JEROME PEULTIER
The infl uence of long-term ageing in NaCl on the passivity and the electrochemical
behaviour of UNS S32304 is studied. The passive fi lm thickness,
the Cr/Fe ratio and the chloride content were signifi cantly increased after
ageing. The chloride distribution depends on residual stresses, sample microstructure
and surface preparation.
Keywords: duplex stainless steel, residual stress, passive fi lm
Pasywacja stali duplex po długim czasie starzenia w 0,5 M NaCl w 50oC
W pracy badano wpływ długiego czasu starzenia w roztworze NaCl na pasywację i
elektrochemiczne zachowanie się stali UNS S32304. Wykazano, że po długim czasie
starzenia znacząco wzrasta grubość warstwy pasywnej, stosunek Cr/Fe i zawartość
chlorków. Rozkład zawartości chlorków zależy od rozkładu narężeń szczątkowych,
mikrostruktury i przygotowania powierzchni.
Słowa kluczowe: stale duplex, naprężenia szczątkowe, warstwa pasywna
ochrona przed korozja 7/2011
1. Introduction
Duplex stainless steels (DSS) are highly
important engineering materials, due to their
generally high corrosion resistance combined
with high strength and moderate alloy cost
(lower nickel and molybdenum content). They
are widely used in various industrial sectors,
such as oil & gas (pipelines and storage tanks),
desalination (evaporators and pumps), pulp
and paper (digester and bleaching reactors)
industries.
DSS have a complex microstructure with
comparable volume of austenite and ferrite.
Due to differences in chemical composition
between austenite and ferrite, a heterogeneous
passive fi lm is formed on both phases [1-3].
In addition, due to differences in mechanical
properties, a heterogeneous stress fi eld may
be generated in metallic grains [4-6]. Under
certain conditions, these differences may also
yield formation of a heterogeneous passive
fi lm.
Microstructural and mechanical changes
and fracture behavior of stainless steels have
widely been studied after long-term ageing at
high [...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2011/7
|
|
|
» Wpływ geometrii kapilary na widma otrzymane techniką lokalnej elektrochemicznej spektroskopii impedancyjnej
|
|
|
VINCENT VIGNAL HALINA KRAWIEC PAULINA ERAZMUS OLIVIER POLITANO
W pracy przedstawiono wpływ geometrii kapilary (średnicy, długości) na
kształt lokalnych widm impedancyjnych zarejestrowanych dla czystej platyny
w 0,1 M roztworze siarczanu VI sodu. Lokalne widma impedancyjne
wykonane za pomocą Techniki Elektrochemicznego Mikro-ogniwa zostały
porównane z widmami zarejestrowanymi w klasycznym trójelektrodowym
układzie.
Słowa kluczowe: lokalna elektrochemiczna spektroskopia impedancyjna,
techniki mikro-kapilarne, elektrochemia na granicy faz
Infl uence of the capillary geometry on the local electrochemical impedance spectroscopy
measurements
In the present paper, the infl uence of the capillary geometry (diameter and length) on
EIS measurements was investigated on pure platinum immersed in 0.1M Na2SO4 solution.
In addition, impedance data obtained using capillaries and the electrochemical
microcell technique were compared to those obtained with a classical three-electrode
cell.
Keywords: local electrochemical impedance spectroscopy, capillary techniques, interfacial
electrochemistry
ochrona przed korozja 7/2011
1. Introduction
Conventional electrochemical impedance
spectroscopy (EIS) has been used for more
than 40 years for studying electrochemical
mechanisms occurring at the electrode/electrolyte
interface. However, this technique is
limited to surface-averaged measurements
which account for the behaviour of the whole
electrode surface. In corrosion problems, such
as in localized corrosion, the response associated
with local phenomena (pitting, crevice
corrosion, breakdown of the passive fi lm, etc.)
cannot be extracted from the global impedance
diagrams. To overcome these diffi culties,
several scanning techniques using microelectrodes
have been developed. Among them, the
local electrochemical impedance spectroscopy
(LEIS) performed on restricted active areas
was pioneered by Isaacs et al. [1-3]. The local
[...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2011/7
|
|
|
|
|
|
» Infl uence of microstructure and Laser Shock Processing (LSP) on the corrosion behaviour of AA2050-T8
|
|
|
VINCENT VIGNAL HASSAN AMAR HALINA KRAWIEC PATRICE PEYRE LUIS FREDERICO DICK
The corrosion behaviour of AA2050-T8 was studied after polishing and after LSP treatment using microcapillaries
and the SVET. After polishing, both pitting at constituent particles and intergranular corrosion were observed. By
contrast, no intergranular corrosion / pits developed in the matrix after LSP. In addition, there is an anodic shift of
the pitting potential of sites containing particles. Benefi cial infl uence of LSP on corrosion behaviour of AA2050-T8
was also demonstrated using the SVET. The local current was systemically lower after LSP treatment.
Keywords: aluminium alloys, SVET, microstructure, corrosion, capillary techniques
Wpływ mikrostruktury i obróbki laserowej (LSP) na korozyjne zachowanie stopu AA2050-T8
Korozyjne zachowanie się stopu aluminium AA2050-T8 było badane po mechanicznym polerowaniu i po obróbce laserowej, za
pomocą Techniki Skaningowej Elektrody Wibrującej (SVET) i mikro-kapilar. Na próbkach polerowanych zaobserwowano korozję
wżerową i międzykrystaliczną w 0,1M NaCl. Z kolei osnowa próbek poddanych obróbce laserowej była odporna na korozję
międzykrystaliczną i wżerową. Dla miejsc zawierających wydzielenia obserwowano przesunięcie potencjału przebicia w kierunku
anodowym. Korzystny wpływ obróbki laserowej na odporność korozyjną stopu aluminium AA2050-T8 wykazały badania za pomocą
SVET. Dla próbek po laserowej obróbce zawsze rejestrowano niższy prąd niż dla próbek polerowanych.
Słowa kluczowe: stopy aluminium, SVET, mikrostruktura, korozja, techniki mikrokapilarne
1. Introduction
Aluminium alloys are a very important category
of materials because of their high mechanical
properties and wide range of industrial
applications. Aluminium alloys are prone to
microstructural corrosion (pitting corrosion,
intergranular corrosion, etc.). Microstructural
corrosion is caused by the presence of intermetallic
particles which may be either anodic
or cathodic with respect to the matrix. Microelectrochemical
techniqu[...]
więcej»
w zeszycie
OCHRONA PRZED KOROZJĄ 2010/11
|
|
|
|
Strona 1
|