» Structure and properties of low temperature nitrided/oxidized NiTi alloy
|
|
Józef Lelątko  Tomasz Goryczka Tadeusz Wierzchoń Maciej Ossowski Bożena Łosiewicz
NiTi alloys have been widely used in biomedical field due to their
shape memory effect, superelasticity and good biocompatibility [1].
They are excellent biomaterials for orthopaedics, dental applications,
vascular and organ surgeries. However, these applications,
especially as a long term implants, require special attention with respect
to nickel ion release into the patient’s metabolism system and
the surrounding tissue. The nickel can cause allergies if persons are
highly sensitive and has a toxic effect on the cell when its concentration
exceeds a certain level [2]. In order to improve the corrosion
resistance of the NiTi alloy and suppress the release of nickel ions,
many surface modification techniques have been used. Titanium
oxide and nitride has been found a good candidate for layers, which
sufficiently protect human body [3, 4]. Additionally, combination
of a layer sequence, forming the titanium oxide and titanium nitride
layers, increases corrosion resistance and biocompatibility [5].
The titanium oxide, especially TiO2 [6], increases the stability of the
surface, creates the physical and chemical barrier against oxygen
migration to the top and limits the way of the nickel oxidation [7].
Low chemical reactivity, high hardness as well as wear and corrosion
resistance are characteristic properties of the titanium nitride
and titanium oxide layers. Reported results show that layers were
thick. Moreover, between the layer and the NiTi matrix a sublayer
of intermetallic phases such as Ni3Ti or Ti2Ni were formed [5, 8].
All phases reveal low plastic properties, which limit their practical
application in the field of medicine where the shape memory effect
or superelasticity is required. Therefore, the formation of very thin
surface layers of TiN, TiO2 or TiN+TiO2 with suitable nanostructure
is the way to improve the biocompatibility of NiTi alloy with shape
memory effect.
In the present work the thin nitride-oxide lay[...]
więcej»
w zeszycie
INŻYNIERIA MATERIAŁOWA 2010/3
|
|
|
|
|
|
|
|
|
» Badanie niskotemperaturowo azotowanych stopów NiTi
|
|
JÓZEF LELĄTKO TOMASZ GORYCZKA TADEUSZ WIERZCHOŃ BOŻENA ŁOSIEWICZ MACIEJ OSSOWSKI EDWARD RÓWIŃSKI HENRYK MORAWIEC
Stopy NiTi o składzie chemicznym zbliżonym do równoatomowego,
wykazujące efekt pamięci kształtu, są znane z licznych zastosowań
w medycynie. Takie właściwości, jak efekt pamięci kształtu,
a w szczególności pseudosprężystość, otwierają szerokie możliwości
ich zastosowania jako biomateriału w ortopedii, stomatologii czy
chirurgii naczyń bądź narządów wewnętrznych [1, 2]. Jednakże zastosowanie
stopów NiTi na długoterminowe implanty budzi wątpliwości
ze względu na ich odporność korozyjną oraz obecność niklu.
W celu ograniczenia korozji i równoczesnego zwiększenia biokompatybilności
powierzchnia stopów pokrywana jest warstwami
ochronnymi. Tlenki tytanu [3, 4], azotki tytanu [5, 6] fazy diamentopodobne
(DLC) [7] okazały się dobrymi materiałami na warstwy,
które skutecznie chronią lud[...]
więcej»
w zeszycie
INŻYNIERIA MATERIAŁOWA 2009/5
|
|
|
|
|
|
|
Strona 1
|
Twój Profil
Twój koszyk