The effect of forming the polyethylene structure of endoprosthesis cups on morphological changes in the upper layer during friction

Czytaj za darmo! »

To increase resistance to wear and permanent deformation of polyethylene working in a polymer/metal couple (e.g. in human joint endoprostheses), the authors applied a new method. The method consists in changing the structure and properties of polyethylene subjected to preliminary work-hardening and irradiation with an electron beam. The assessment of the morphology obtained for the material v[...]

The morphology, texture and structure orientation of polyethylene formed via work hardening and electron irradiation

Czytaj za darmo! »

The paper presents a new method for shaping the structure and properties of polyethylene intended for endoprostheses' cups. The method consists in applying plastic strain to a semi-finished product of a cup (Chirulen) and its irradiation with an electron beam. As a result of a small, permanent deformation, performed in an area distant from the consolidation area and a high polymer orien[...]

Analysis of the possibilities of increasing resistance to plastic deformation of new biopolymers by means of modification through radiation

Czytaj za darmo! »

Operational durability of the polymer-metal kinematic systems used in technology and endoprosthesoplasty depends to a considerable degree on the resistance of polyethylene to plastic deformation and wear [1÷6]. In about 90% of applications, conventional and the cheapest polymer-metal couples are still used in alloplastic procedures. In one of such cases, a ca. fivefold reduction of susceptibility to permanent deformation and tribological wear was obtained for the polyethylene Chirulen 1120. The effect was a result of a combined application of small plastic deformation (ef. ≈ 0.2, initiating the transitions) and electron beam irradiation [7÷9]. Those factors modified the morphology of the polymer. As a result, in operational conditions, the thickness of the deformed upper layer of polyethylene reduced, its degree of crystallinity and reorientation of the lamellar phase were modified, the degree of structure order increased, and in consequence, the operational durability improved. The reference literature of the last decade shows, however, that in order to increase resistance to wear and ageing, what should be aimed at is to ensure a very high molecular weight and an appropriate proportion of crystalline and amorphous phases [10÷13]. In the shaping of the properties, a more and more significant role of irradiation with an electron beam is being recognized. Doses higher than 25 kGy are conducive to decomposition of long macrochains, spatial arrangement of the structure and UHMWPE crosslinking. A growing dose, to as much as 150 kGy, causes a very significant increase of resistance to wear [14, 15]. According to the presented information from the reference literature, two grades of polyethylene have been recently introduced to production. Polymers GUR 1020 and GUR 1050 have replaced Chirulen 1120 of a molecular weight of ca. 106 g/mole. New materials weigh many times more: 5·106 and 9.2·106 g/mole, and are intended e[...]