Infl uence of microstructure and Laser Shock Processing (LSP) on the corrosion behaviour of AA2050-T8

nr katalogowy: 55611

The corrosion behaviour of AA2050-T8 was studied after polishing and after LSP treatment using microcapillaries and the SVET. After polishing, both pitting at constituent particles and intergranular corrosion were observed. By contrast, no intergranular corrosion / pits developed in the matrix after LSP. In addition, there is an anodic shift of the pitting potential of sites containing particles. Benefi cial infl uence of LSP on corrosion behaviour of AA2050-T8 was also demonstrated using the SVET. The local current was systemically lower after LSP treatment. Keywords: aluminium alloys, SVET, microstructure, corrosion, capillary techniques Wpływ mikrostruktury i obróbki laserowej (LSP) na korozyjne zachowanie stopu AA2050-T8 Korozyjne zachowanie się stopu aluminium AA2050-T8 było badane po mechanicznym polerowaniu i po obróbce laserowej, za pomocą Techniki Skaningowej Elektrody Wibrującej (SVET) i mikro-kapilar. Na próbkach polerowanych zaobserwowano korozję wżerową i międzykrystaliczną w 0,1M NaCl. Z kolei osnowa próbek poddanych obróbce laserowej była odporna na korozję międzykrystaliczną i wżerową. Dla miejsc zawierających wydzielenia obserwowano przesunięcie potencjału przebicia w kierunku anodowym. Korzystny wpływ obróbki laserowej na odporność korozyjną stopu aluminium AA2050-T8 wykazały badania za pomocą SVET. Dla próbek po laserowej obróbce zawsze rejestrowano niższy prąd niż dla próbek polerowanych. Słowa kluczowe: stopy aluminium, SVET, mikrostruktura, korozja, techniki mikrokapilarne 1. Introduction Aluminium alloys are a very important category of materials because of their high mechanical properties and wide range of industrial applications. Aluminium alloys are prone to microstructural corrosion (pitting corrosion, intergranular corrosion, etc.). Microstructural corrosion is caused by the presence of intermetallic particles which may be either anodic or cathodic with respect to the matrix. Microelectrochemical techniqu[...]

Jeśli masz wykupiony/przyznany dostęp - zaloguj się. Skorzystaj z naszych propozycji zakupu!

Publikacja


e-Publikacja (format pdf) - nr 55611 "Infl uence of microstruct..." licencja: Osobista Produkt cyfrowy	10.00 zł

Zeszyt


OCHRONA PRZED KOROZJĄ - e-zeszyt (pdf) 2010-11 licencja: Osobista Produkt cyfrowy	42.00 zł

Prenumerata

OCHRONA PRZED KOROZJĄ - prenumerata cyfrowa
licencja: Osobista

Produkt cyfrowy
Nowość

504.00 zł

OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna + wysyłka
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - papierowa prenumerata roczna	636.00 zł brutto 588.89 zł netto 47.11 zł VAT (stawka VAT 8%)
OCHRONA PRZED KOROZJĄ - pakowanie i wysyłka	42.00 zł brutto 34.15 zł netto 7.85 zł VAT (stawka VAT 23%)

678.00 zł

OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS
licencja: Osobista

Szczegóły pakietu

Nazwa
OCHRONA PRZED KOROZJĄ - PAKIET prenumerata PLUS (Prenumerata papierowa + dostęp do portalu sigma-not.pl + e-prenumerata)	762.00 zł brutto 705.56 zł netto 56.44 zł VAT (stawka VAT 8%)

762.00 zł

Zeszyt

2010-11

Twój Koszyk

Publikacja

Zeszyt

Prenumerata

Zeszyt

Czasopisma